Tungsten Contact Disc/part
- Apr 21, 2017 -

    A tungsten contact disc is treated by burnishing, so as to smooth and compact the contact surface and remove the surface-crazed metals and oxides, while simultaneously filling the surface pores with a contaminant such as iron. The contaminants present in the pores are subsequently removed by immersing the contact disc in a dissolving agent, and the remaining natural oxides of the tungsten are removed from the walls of the pores by cathodic reduction, to create large pore sites, which are free of oxides and contaminants.

Electric purpose tungsten contact

 2.jpg

Purity W1≥99.95%
Specific gravity ≥19.1g/cm3~19.3 g/cm3
Crystal grain number ≥ 10,000PCS/mm2
Hardness  ≥ 71-74HRA
Size allowable tolerance d.h±0.05mm (It can produce the goods according to the client's specific drawings.)
Seat nail material is low carbon steel whose carbon content is equal to or less than 0.10%.
The copper purity of copper welding material is equal to or larger than 99.95%.
Welding point strength ≥ 83MPa
It strictly produces the goods according to P.R. China Mechanical Industry Standard.

Electric purpose tungsten sheet

 1.jpg

Purity W1≥99.95%
Specific gravity ≥19.1g/cm3
19.3g/cm3
Crystal grain number ≥10,000 a/mm2
Hardness ≥71-74HRA
Size allowable tolerance d.h±0.05mm(It can produce the goods according to the client's coming drawings.)
The current regular specifications:
Diameter: Φ3.0mm
Φ10.0mm
Thickness: Above h0.5mm
Spherical surface: SR13mm
50mm
Special requirement size allowable tolerance can be d.h±0.02mm

 

Welcome to your inquiry, we will quote you best price.

 

 

Baoji Hanz Material Technology Co., Ltd.

Tel:+86-917-3258886

Fax:+86-917-3258889 

Whatsapp,Wechat, Mobile:+86 18091719909

Email:  admin@hanztech.cn


Copyright © Baoji Hanz Material Technology Co.,Ltd